During the operation of a PEMFC, the polymer membrane is degraded by electrochemical reactions and mechanical stresses. We investigated the effects of repeated electrochemical and mechanical degradations in a membrane. For mechanical degradation, the membrane and MEA were repeatedly subjected to wet/dry cycles; for electrochemical degradation, the cell was operated under open-circuit voltage (OCV)/low-humidity conditions. The repeated wet/dry cycles led to a decrease in the mechanical strength of the membrane. When the MEA was degraded electrochemically, repeated wet/dry cycling resulted in the formation of pinholes in the membrane. In the case of different MEAs that were first degraded electrochemically, the extents of their hydrogen crossover currents increased due to repeated wet/dry cycling being different. Therefore, these results indicated that the membrane durability could be evaluated by these methods of repeated electrochemical degradation and wet/dry cycles.

Polymer Electrolyte Membrane Fuel Cell Durability Membrane Degradation Mechanical Degradation Wet/Dry Cycling

Uribe FA, Gottesfeld S, Zawodzinski TA, J. Electrochem. Soc., 149(3), A293 (2002)
Okada T, Handbook of Fuel Cells vol.3, John Wiley & Sons Ltd., Chichester, Elgland, 627 (2003)
Kienitz BL, Baskaran H, Zawodzinski TA, Electrochim. Acta, 54(6), 1671 (2009)
Okada T, Satou H, Okuno M, Yuasa M, J. Phys. Chem. B, 106(6), 1267 (2002)
Laconti AB, Hamdan M, McDonald RC, Handbook of Fuel Cells vol.3, John Wiley & Sons Ltd., Chichester, Elgland, 647 (2003)
Mittal VO, Kunz HR, Fenton JM, Electrochem. Solid State Lett., 9(6), A299 (2006)
Liu W, Zuckerbrod D, J. Electrochem. Soc., 152(6), A1165 (2005)
Endoh E, Terazono S, Widjaja H, Takimoto Y, Electrochem. Solid State Lett., 7(7), A209 (2004)
Wahdame B, Candusso D, Harel F, Francois X, Pera MC, Hissel D, Kauffmann JM, J. Power Sources, 182(2), 429 (2008)
Dong Q, Mench MM, Cleghorn S, Beuscher U, J. Electrochem. Soc., 152(11), A2114 (2005)
Teranishi K, Kawata K, Tsushima S, Hirai S, Electrochem. Solid State Lett., 9(10), A475 (2006)
Ohma A, Suga S, Yamamoto S, Shinohara K, J. Electrochem. Soc., 154(8), B757 (2007)
Yu HM, Ziegler C, J. Electrochem. Soc., 153(3), A570 (2006)
Ralph TR, Barnwell DE, Bouwman PJ, Hodgkinson AJ, Petch MI, Pollington M, J. Electrochem. Soc., 155(4), B411 (2008)
Mathias MF, Makharia R, Gasteiger HA, Conley JJ, Fuller TJ, Gittleman CJ, Kocha SS, Miller DP, Mittelsteadt CK, Xie T, Yan SG, Yu PT, Electrochem. Soc. Interface., 14(3), 24 (2005)
Tang HL, Shen PK, Jiang SP, Fang W, Mu P, J. Power Sources, 170(1), 85 (2007)
Huang XY, Solasi R, Zou Y, Feshler M, Reifsnider K, Condit D, Burlatsky S, Madden T, J. Polym. Sci. B: Polym. Phys., 44(16), 2346 (2006)
Chen C, Fuller TF, Polymer Degradation and Stability., 94, 1436 (2009)