articles This is an Open-Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/bync/3.0) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
Copyright © KIChE. All rights reserved.

All issues

조합화학을 이용한 Y(As, Nb, P, V)O4 청색 발광 형광체의 합성 및 광 특성 분석

Synthesis and Luminescent Properties Analysis of Y(As, Nb, P, V)O4 Blue Emitting Phosphors by Combinatorial Chemistry Method

충남대학교 화학공학과, 대전 305-764 1순천대학교 재료공학부, 순천 540-742 2한국화학연구소, 대전 305-600
Dept. of Chemical Engineering, Chungnam National University, Daejeon 305-764, Korea 1Materials Science and Metallurgical Engineering, Sunchon National University, Sunchon 540-742, Korea 2Korea Research Institute of Chemical Technology, Daejeon 305-600, Korea
s0909iw@orgio.net
HWAHAK KONGHAK, February 2002, 40(1), 63-69(7), NONE
downloadDownload PDF

Abstract

조합화학기법을 이용하여 청색 발광을 하는 YRO4(R=As, Nb, P, V)계 형광체를 합성하였다. 합성한 형광체는 254 nm 및 147 nm 여기 하에서의 발광 세기에 관한 사면체 라이브러리를 완성하였다. 254 nm로 여기 시켰을 때, YAsO4를 중심으로 높은 발광 세기를 보였고, Y(As0.4P0.4V0.2)O4의 조성으로 1,200 ℃에서 합성하였을 때 가장 높은 발광 세기를 보였다. 그러나, 147 nm로 여기시켰을 경우에는 YPO4를 중심으로 해서 높은 발광 세기를 나타내었다.
The YRO4(R=As, Nb, P, V) blue emitting phosphors were prepared by the combinatorial chemistry method. The quaternary combinatorial library was designed to investigate the luminescence of the host material under UV and VUV excitations(254, 147 nm). In view of the luminescence yield, YAsO4 rich region was found to be optimum under 254 nm excitation._x000D_ It was found that the phosphor synthesized at 1,200 ℃ with Y(As0.4P0.4V0.2)O4 composition had a maximum emission intensity. However, the results under 147 nm excitation were different from those of 254 nm excitation, the samples of the composition containing a large amount of YPO4 shows the high emission intensity.

References

Lee JS, J. Information Display, 1, 25 (2000)
Moon SI, Shin YY, Heo YD, Kim YH, Gong MS, Chem. World, 37, 26 (1997)
Danielson E, Golden JH, Mcfarland EW, Reaves CM, Weinberg WH, Wu XD, Nature, 389(6654), 944 (1997) 
Wang JS, Yoo Y, Gao C, Takeuchi I, Sun XD, Chang HY, Xiang XD, Schultz PG, Science, 279(5357), 1712 (1998) 
McFarland WW, Weinberg WH, Trends Biotechnol., 17, 107 (1999) 
Osvaldo AS, Simone AC, Renata RI, J. Alloy. Compd., 303, 316 (2000) 
Dinesh KA, William BW, J. Electrochem. Soc., 133, 1261 (1986) 
Han CH, Kim HJ, Chang H, Lee SK, Park JD, J. Electrochem. Soc., 147(7), 2800 (2000) 
Blasse G, Bril A, J. Chem. Phys., 50, 2974 (1969) 
Ropp RC, J. Electrochem. Soc., 115, 841 (1986) 
Rambabu U, Amalnerkar DP, Kale BB, Buddhudu S, Mater. Chem. Phys., 70, 1 (2001) 
Rambabu U, Buddhudu S, Opt. Mater., 17, 401 (2001) 
Zeon IW, Sohn KS, Jeong YS, Kim CH, Park HD, Ryu SG, Korean J. Mater. Res., 11(3), 227 (2001)
Blasse G, Grabmaier BC, "Luminescent Materials," Germany (1994)

The Korean Institute of Chemical Engineers. F5, 119, Anam-ro, Seongbuk-gu, 233 Spring Street Seoul 02856, South Korea.
Phone No. +82-2-458-3078FAX No. +82-507-804-0669E-mail : kiche@kiche.or.kr

Copyright (C) KICHE.all rights reserved.

- Korean Chemical Engineering Research 상단으로