This is an Open-Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/bync/3.0) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.

All issues

HNBR compound와 RFL 처리된 Polyester 섬유의 접착 연구

Adhesion Between HNBR Compound and Polyester Fabric Treated with RFL

이주희 강윤희 박득주 김욱수 손우정¹ 변영후² 김원호^†

Juhui Yi Yun-Hee Kang Deuk-Joo Park Wook-Soo Kim Woo Jeong Son¹ Young-Hoo Byun² Wonho Kim^†

부산대학교 화공생명공학부, 609-735 부산광역시 금정구 장전동 산 30 ¹(주)동일고무벨트 기술연구소, 609-808 부산광역시 금정구 금사동 7 ²(주)대영특수고무 기술연구팀, 619-962 부산광역시 기장군 정관면 모전리 17

Department of Chemical Engineering, Pusan National University, Jangjeon-dong, Geumjeong-gu, Busan 609-735, Korea ¹DRB Co., Ltd, 7 Geumsa-dong, Geumjeong-gu, Busan 609-808, Korea ²Dae Young Special Rubber Co.,Ltd, 17 Mojeon-Ri, Jeonggwan-myeon, Gijang-gun, Busan 619-962, Korea

whkim@pusan.ac.kr

Korean Chemical Engineering Research, October 2010, 48(5), 568-573(6), NONE Epub 17 November 2010

Download PDF

Abstract

본 연구에서는 polyester 섬유표면에 활성기를 부여하기 위한 전처리제로 isocyanate를 이용하여 농도에 따른 접착력을 평가하였다. 이 후 HNBR compound와 polyester fabric의 접착 시 접착력이 우수한 RFL 용액용 latex 선정 및 F/R mole ratio, F/R resin/latex 무게 비에 따른 실험을 진행하였다. 그 결과 전처리제의 농도가 7 wt%인 경우 가장 높은 접착력을 나타내었으며, RFL 용액용 latex로는 HNBR 컴파운드와 상용성이 높은 NBR latex가 우수한 결과를 나타내었고 F/R mole ratio, FR resin/latex 무게비가 각각 1/1, 20%일 때 가장 높은 접착력을 나타내었다. 또한, peel test와 FTIR 분석을 이용해 RF resin의 열처리 온도에 따른 접착강도와 spectra의 peak 변화를 평가해 본 결과 최적의 열처리 온도는 200 ℃이었다.

Adhesive strength was evaluated for the polyester fabric treated with various concentration of polymeric isocyanate to introduce functional group on the surface. Also experiments were performed to find out the type of latex, F/R mole ratio, and FR resin/latex weight ratio for the RFL solution to optimize adhesion between HNBR compound and the treated polyester fabric. Optimum adhesion strength was obtained when 7 wt% of the concentration of polymeric isocyanate, NBR latex because of the compatibility of HNBR compound, 1/1 of F/R mole ratio, and 20 wt% of FR resin/latex were applied. Optimum cure temperature for the RFL solution was 200 ℃ according to the results of peel test and the reason was determined by analyzing the ATR FTIR spectra of the RF resin according to the curing temperature.

Keywords

HNBR Polyester Fabric RFL Isocyanate

References

Weir RJ, Blackshaw GC, International Rubber Conference, Sydney, Australia (1988)
Takeyama T, Matsui J, Rubber Chem. Technol., 42, 159 (1969)
Brinke JW, Debnath SC, Reuvekamp LAEM, Noordermeer JWM, Composites Sci. Technol., 63, 1165 (2003)
Wennekes WB, Datta RN, Noordermeer JWM, Kautschuk Gummi Kunststoffe, 60, 20 (2007)
Wennekes WB, Datta RN, Noordermeer JWM, Rubber Chem. Technol., 80, 565 (2007)
Wennekes WB, Datta RN, Noordermeer JWM, Rubber Chem. Technol., 81, 523 (2008)
Durairaj RB, Resorcinol: Chemistry, Technology and Application, Springer, 189-276 (2005)
Wootton DB, The application of textiles in rubber, Rapra Technology Limited, 30-40 (2001)
Shoaf CJ, Patent No. 3307966 (1963)
Moult RH, Handbook of adhesive, Van Nostrand Teinhold Company, 418-419 (1985)
Angier DJ, Watson WF, J. Polym. Sci., 18, 129 (1955)