This is an Open-Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/bync/3.0) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.

All issues

유-무기 하이브리드 코팅 용액을 이용한 고굴절 하드코팅 막의 제조

Preparation of Hard Coating Films with High Refractive Index using Organic-Inorganic Hybrid Coating Solutions

최진주 김남우 안치용 송기창^†

Jin Joo Choi Nam Uoo Kim Chi Yong Ahn Ki Chang Song^†

건양대학교 화공생명학과, 충남 논산시 대학로 121

Department of Chemical and Biochemical Engineering, Konyang University, 121 Daehak-ro, Nonsan, Chungnam 320-711, Korea

Korean Chemical Engineering Research, June 2014, 52(3), 388-394(7), 10.9713/kcer.2014.52.3.388 Epub 2 June 2014

Download PDF

Abstract

출발물질인 TTIP로부터 이산화티탄 졸을 합성하여 무기물로 사용하고 유기물로서 실란커플링제인 methacryloxypropyl trimethoxysilane (MPTMS), aminopropyl triethoxysilane (APS), glycidoxypropyl trimethoxysilane (GPTMS), vinyltriethoxysilane (VTES)을 2종 혹은 3종씩 복합 사용하여 유-무기 하이브리드 코팅 용액을 제조하였다. 그 후 코팅 용액을 기재인 PC시트 위에 스핀 코팅시키고, 열경화 시켜 하드코팅 막을 제조하였다. 2종 실란커플링제를 혼합하여 제조된 코팅 막들은_x000D_ 기재와의 부착력과 연필경도가 우수하지 못했으나, 3종 실란커플링제를 혼합하여 제조한 코팅 막은 2H~4H의 향상된 연필경도와 5B의 우수한 부착력을 나타내었다. 이산화티탄 졸의 첨가량이 20 g인 코팅 막의 굴절률은 550 nm에서 1.56을 나타내었으나 이산화티탄 졸의 첨가량을 20 g에서 30 g으로 증가시킨 경우, 코팅 막의 굴절률이 1.63으로 향상되었다.

Inorganic-organic hybrid coating solutions were synthesized using titania sol from titanium isopropoxide (TTIP) as an inorganic component and mixture of two or three types of silane coupling agents, such as methacryloxypropyl trimethoxysilane (MPTMS), aminopropyl triethoxysilane (APS), glycidoxypropyl trimethoxysilane (GPTMS) and vinyltriethoxysilane (VTES) as an organic component. The hard coating films were obtained by spin-coating on the_x000D_ polycarbonate sheets and curing the inorganic-organic hybrid coating solutions. The coating films made from the mixture of two types of silane coupling agents showed poor pencil hardness and adhesion, while those from the mixture of three types of silane coupling agents exhibited an improved pencil hardness of 2H?4H and adhesion of 5B. The refractive indexes of coating films were increased from 1.56 to 1.63 at 550 nm by increasing the content of titania sols from 20 to 30 g.

Keywords

Inorganic-organic Hybrid Coating Solutions Hard Coating Films Titania Sol Silane Coupling Agent High Refractive Index

References

Lee MS, Jo NJ, J. Korean Ind. Eng. Chem., 12(6), 643 (2001)
Kwak S, Shim J, Yoon HG, Lee KH, Polym. Sci. Technol., 14(2), 181 (2003)
Mackenzie JD, Bescher EP, J. Sol-Gel Sci. Tech., 19, 23 (2000)
Schottner G, Rose K, Posset U, ibid., 27, 71 (2003)
Kim SW, Korean J. Chem. Eng., 28(1), 298 (2011)
Cheong IY, Cho KI, Cheong SH, Park HN, Song KC, Korean Chem. Eng. Res., 45(4), 335 (2007)
ASTM D 3359, “Standard Test Methods for Measuring Adhesion by Tape Test,” ASTM International, 927-929 (1997)
Song KC, Pratsinis SE, J. Colloid Interface Sci., 231(2), 289 (2000)
Ji YJ, Shin YJ, Shin YR, Kim JY, Yoon YS, Shin JS, J. Adhesion & Interface, 7, 10 (2006)
Park SJ, Jin JS, Lee JR, J. Korean Ind. Eng. Chem., 12(2), 143 (2001)
Lee SY, “A Study on Preparation of Organic-Inorganic Hybrid Films using Sol-Gel Method,”Master Dissertation, KAIST, Daejeon (1998)